Liquid state dependent solidification of a Co-B eutectic alloy under a high magnetic field

Résumé

The structure transition inside the Co-81.5at.%B alloy liquid has been studied by an in-situ magnetization measurement. A crossover was observed on the 1/ M - T curve during the overheating process, indicating that a liquid-liquid structure transition (LLST) took place in the melt. Based on this information, the effects of LLST on the solidification behavior, microstructure and tribology property were investigated experimentally. The sample solidified with the LLST exhibits significantly different solidification behaviors, i.e., the nucleation undercooling and the recalescence extent are conspicuously enlarged, and the solidification time is shortened. As a result, the microstructure is effectively refined and homogenized, and the hardness and wear resistance are significantly enhanced. The present work might be helpful for not only theoretically understanding the influence of LLST on the solidification behavior but also providing an alternative approach to tailor the microstructure and properties. (c) 2022 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.
Fichier non déposé

Dates et versions

hal-03878222 , version 1 (29-11-2022)

Identifiants

Citer

Yixuan He, Fan Bu, Yuhao Wu, Jianbao Zhang, Dawei Luo, et al.. Liquid state dependent solidification of a Co-B eutectic alloy under a high magnetic field. Journal of Materials Science and Technology, 2022, 116, pp.58-71. ⟨10.1016/j.jmst.2021.11.037⟩. ⟨hal-03878222⟩
21 Consultations
0 Téléchargements

Altmetric

Partager

More