Rheological Characterization of High Molecular Weight PEO-An Extensive Parametric Experimental Study

Caractérisation rhéologique du PEO de grande mass moléculaire - Etude expérimentale paramétrique exhaustive

Résumé

Abstract A comprehensive study of the rheological characterization of the aqueous solutions of PEO (Polyethylene Oxide) with molecular mass of 4×10^6, 5×10^6 and 8×10^6 g/mol respectively named (4miDA), (5miDA) and (8miDA) was conducted. A large batch of samples of 4miDA PEO with concentrations varying from 0.1% to 3% representing the range of dilute solutions to very high viscous hydrated gels, were tested. Steady state shear flow and oscillatory measurements are reported. Cross, Carreau and Carreau-Yasuda models were used to describe the shear-thinning behaviour within the shear rate range (0.001 ≤ γ• ≤ 3000 s-1). Experimental findings were validated with published results under the same operating conditions within specified shear rate ranges (0.1≤ γ• ≤100 s-1). We find that the behaviour of PEO under shear is highly dependent on the rheometer, material and operating procedures. Oscillatory measurements were carried out to determine the complex properties of the PEO solutions in the frequency ω and strain amplitude γ ranges of (0.01 ≤ ω ≤100 rad/s) and (0.01 ≤ γ ≤1000 %), respectively. Higher magnitudes of dynamic moduli (G' & G''), zero (η0) and infinite (η∞) shear rate viscosities, resonant frequencies (ωres), linear viscoelastic regions (LVER), and higher relaxation time constants (λ) were observed with increasing concentration and molecular weight. The rheological response of the PEO polymeric solutions was further clarified via Lissajous curves. The aim of this work is to characterize the behaviour of the 4miDa PEO prior to its use in an experimental investigation of the secondary flows of viscoelastic fluids in non-circular channels.
Fichier principal
Vignette du fichier
FMANU-FE-22-1314.pdf (2.05 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03859954 , version 1 (18-11-2022)

Identifiants

Citer

Hafiz Ahmad, M’hamed Boutaous, Shihe Xin, Hervé Pabiou, Dennis A Siginer. Rheological Characterization of High Molecular Weight PEO-An Extensive Parametric Experimental Study. Journal of Fluids Engineering, 2023, 145 (2), pp.021204. ⟨10.1115/1.4056160⟩. ⟨hal-03859954⟩
20 Consultations
119 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More