Effect of strain and stoichiometry on the ferroelectric and pyroelectric properties of the epitaxial Pb(Zr0.2Ti0.8)O-3 films deposited on Si wafers
Résumé
Properties of epitaxial PbZr0.2Ti0.8O3 (PZT) films deposited on Si substrates were investigated for integration in the present CMOS technology. Polarization is downward oriented, in association with the presence of an internal electric field, and has a lower value compared to the PZT films deposited on single crystal perovskite SrTiO3 (STO) substrates (40 mu C/cm(2) versus 80 mu C/cm(2)), while the dielectric constant is larger (180 versus 120). Large value for the pyroelectric coefficient was also found, 1.22 x 10(-3)C/m(2)K, as for PZT grown on single crystal STO. The macroscopic ferroelectric and pyroelectric properties appear to be affected by the structural quality and stoichiometry of the PZT film. The changes in the electric properties are an effect of the strain gradients induced by the large difference between the thermal expansion coefficients of PZT and Si substrate, leading in turn to Pb oxidation and antisite defect formation compared to PZT films deposited on STO substrates.