475 °C Embrittlement in a duplex stainless steel UNS S31803

Résumé

The susceptibility of a duplex stainless steel UNS S31803 to thermal embrittlement at 475 °C was evaluated by means of mechanical tests (impact energy and hardness), magnetic measurements (hysteresis and thermomagnetic analysis) and scanning electron microscopy. The results show that the material undergoes severe embrittlement and hardening in the first 100 h. The corrosion resistance of the ferrite phase in a 10%HNO3 + 0.05%HF solution deteriorated after 500 h of ageing. The Curie temperature (Tc) was the most sensitive magnetic property to the microstructural changes that promote embrittlement. Tc increases with ageing time due to the progressive reduction of chromium in the Fe-rich matrix during spinodal decomposition.
Fichier principal
Vignette du fichier
pdf(12).pdf (143.89 Ko) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-03606049 , version 1 (11-03-2022)

Licence

Paternité - Pas d'utilisation commerciale

Identifiants

Citer

S.S.M. Tavares, R.F. De Noronha, M.R. Da Silva, J.M. Neto, Sébastien Pairis. 475 °C Embrittlement in a duplex stainless steel UNS S31803. Materials Research, 2001, 4 (4), pp.237-240. ⟨10.1590/S1516-14392001000400003⟩. ⟨hal-03606049⟩

Collections

CNRS
2 Consultations
16 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More