Synthesis, Sintering, and Electrical Properties of BaCe0.9−xZrxY0.1O3−δ

Résumé

BaCe0.9−xZrxY0.1O3−δ powders were synthesized by a solid-state reaction. Different contents of cerium and zirconium were studied. Pellets were sintered using either conventional sintering in air at 1700◦C or the Spark Plasma Sintering (SPS) technique. The density of the samples sintered by SPS is much higher than by conventional sintering. Higher values of ionic conductivity were obtained for the SPS sample.

Mots clés

Matériaux

Domaines

Matériaux
Fichier principal
Vignette du fichier
Ricote_2412.pdf (1.91 Mo) Télécharger le fichier
Origine Fichiers éditeurs autorisés sur une archive ouverte

Open Archive Toulouse Archive Ouverte (OATAO)  : Connectez-vous pour contacter le contributeur

https://hal.science/hal-03590663

Soumis le : lundi 28 février 2022-09:30:58

Dernière modification le : mercredi 4 décembre 2024-14:44:02

Télécharger pour visualiser

Dates et versions

hal-03590663 , version 1 (28-02-2022)

Identifiants

Citer

Sandrine Ricote, Gilles Caboche, Claude Estournès, Nikolaos Bonanos. Synthesis, Sintering, and Electrical Properties of BaCe0.9−xZrxY0.1O3−δ. Journal of Nanomaterials, 2008, 2008, pp.0. ⟨10.1155/2008/354258⟩. ⟨hal-03590663⟩

Exporter

BibTeX XML-TEI Dublin Core DC Terms EndNote DataCite

Collections

UNIV-BOURGOGNE CNRS ICB TOULOUSE-INP UNIV-UT3 UT3-TOULOUSEINP CIRIMAT
5 Consultations
25 Téléchargements

Altmetric

Partager

More