Determination of residual stress gradient in a Ti-stabilized austenitic stainless steel cladding candidate after carburization in liquid sodium at 500 °C and 600 °C - Archive ouverte HAL Access content directly
Journal Articles Acta Materialia Year : 2021

Determination of residual stress gradient in a Ti-stabilized austenitic stainless steel cladding candidate after carburization in liquid sodium at 500 °C and 600 °C

Abstract

Non-destructive residual stress profile measurement with a micrometric depth resolution within the depth of carburized Ti-stabilized stainless steel cladding candidate was carried out by high-energy X-ray diffraction. The samples were carburized in carburizing nuclear liquid sodium at 500 °C and 600 °C for 1000 h. The full residual stress tensor profile was determined thanks to the estimation of the strain-free lattice parameter evolution using the carbon concentration profile measured by electron probe microanalysis and thermodynamic simulation. For the sample carburized at 500 °C, the residual stress genesis was governed by the carbon concentration within the steel and the formation of expanded austenite. For the sample carburized at 600 °C, the residual stress profile in the austenitic matrix depended on the precipitation of M23C6 carbide. Stress relaxation was observed in the intragranular carburization zone. For the two temperatures, compressive residual stresses developed in the carburized zone and tensile stresses developed in the rest of the sample.
Fichier principal
Vignette du fichier
Slim_28774.pdf (2.76 Mo) Télécharger le fichier
Origin : Files produced by the author(s)

Dates and versions

hal-03588958 , version 1 (25-02-2022)

Licence

Attribution - NonCommercial - NoDerivatives

Identifiers

Cite

Mohamed Fares Slim, Guillaume Geandier, Fabien Rouillard, Benoît Malard. Determination of residual stress gradient in a Ti-stabilized austenitic stainless steel cladding candidate after carburization in liquid sodium at 500 °C and 600 °C. Acta Materialia, 2021, 221, pp.117435. ⟨10.1016/j.actamat.2021.117435⟩. ⟨hal-03588958⟩
32 View
13 Download

Altmetric

Share

Gmail Facebook Twitter LinkedIn More