Influence of hydrogen vacancy interactions on natural and artificial ageing of an AlMgSi alloy

Guillaume Hachet
Xavier Sauvage

Résumé

The influence of hydrogen on the structural evolutions of an Al-Mg-Si alloy during natural and artificial ageing was investigated experimentally. The aim of the study was a better understanding of interactions between hydrogen and crystalline defects and especially vacancies. Experimental data demonstrate that during natural ageing in hydrogen environment, the hardening response is delayed. This is attributed to a slower recovery of excess vacancies linked to a lower mobility. To confirm and quantify the influence of hydrogen on the vacancy migration energy, artificial ageing was carried out in conditions where the vacancy concentration is constant. Hence, long-time annealing treatments were carried out to investigate the influence of hydrogen on the coarsening of rod-shaped precipitates. Using transmission electron microscopy and atom probe tomography, it was demonstrated that the precipitate volume fraction and composition are unchanged under H2 atmosphere but the coarsening kinetic is significantly reduced. This leads to a delayed softening, in good agreement with theoretical estimates. Thus, even a low concentration of hydrogen in solid solution significantly affects the mobility of alloying elements in the aluminium matrix. This is the result of hydrogen-vacancy interactions that lead to an increase of the vacancy migration energy. Based on classical coarsening theories, it was possible to demonstrate that this increase is of about 5% for a concentration of hydrogen close to the vacancy concentration.
Fichier principal
Vignette du fichier
Revised_manuscript.pdf (850.68 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03588581 , version 1 (25-02-2022)

Identifiants

Citer

Guillaume Hachet, Xavier Sauvage. Influence of hydrogen vacancy interactions on natural and artificial ageing of an AlMgSi alloy. Journal of Alloys and Compounds, 2022, 905, pp.164251. ⟨10.1016/j.jallcom.2022.164251⟩. ⟨hal-03588581⟩
35 Consultations
67 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More