Adhesion characterization of SiO2 thin films evaporated onto a polymeric substrate

Résumé

To ensure good adhesion between a 200 nm thick silicon dioxide layer and a 4.5 μm thick hardcoat polymeric coating, a better understanding of mechanisms of adhesion at this interface is needed. To reach this purpose, focus is placed on two axes: characterizing mechanical properties of materials composing the system and in parallel, finding an applicable and effective method to quantify adhesion. Small dimension of SiO2 thin film makes it challenging to accurately characterize it. Hence the use of both nano-indentation and AFM to attempt assessment of SiO2 thin film elastic modulus Ef; taking into account limitations and uncertainty associated with each technique. Elastic modulus of SiO2 thin film determined by nano-indentation is roughly 50 GPa on a wafer substrate and 15 GPa on a lens substrate. As for AFM, modulus measured is approximatively 56 GPa on a wafer substrate and 22 GPa on a lens substrate. This highlights significant influence of substrate for both techniques. Impact on mechanical properties between SiO2 thin films under different intrinsic stresses was also investigated. Results suggest that higher density of SiO2 thin film leads to higher elastic modulus. To quantify adhesion, micro-tensile and micro-compression tests were performed. Micro-tensile experiments give ultimate shear strengths of hardcoat-substrate interface ranging from 9 to 14 MPa. Values of energy release rates of SiO2 / Hardcoat, range from 0.1 J/m² to 0.5 J/m², depending on moduli values found on wafer or lens substrate.
Fichier principal
Vignette du fichier
Ho_21048.pdf (544.59 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03510157 , version 1 (04-01-2022)

Identifiants

Citer

Caroline Ho, Anita Dehoux, Loïc Lacroix, Joël Alexis, Olivier Dalverny, et al.. Adhesion characterization of SiO2 thin films evaporated onto a polymeric substrate. International Journal of Engineering Research & Science, 2018, 4 (2), pp.38-46. ⟨10.5281/zenodo.1187695⟩. ⟨hal-03510157⟩
35 Consultations
16 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More