Surface tension, interfacial segregation and graphite shape in cast irons

Résumé

Using literature data on iron melts, an expression of the surface tension of cast iron melts as a function of temperature and composition was obtained. Its predictions were satisfactorily compared with reported experimental results. Then, an analysis of experimental information of sessile drop experiments with cast iron melts onto graphite substrates showed a strong adhesion between these two phases when sulfur is present, and its dramatic decrease when the sulfur activity is reduced by the addition of spheroidizers such as Mg and Ce. Finally, analysis and discussion of results on the segregation of impurities and trace elements at the graphite matrix interface in cast irons led to the proposal of a scheme for their effect on graphite shape.

Domaines

Matériaux
Fichier principal
Vignette du fichier
Adsorption and barrier effect HAL.pdf (548.16 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03437449 , version 1 (19-11-2021)

Identifiants

Citer

J. Lacaze, O Dezellus. Surface tension, interfacial segregation and graphite shape in cast irons. Metallurgical and Materials Transactions B, 2021, 53, pp.161-177. ⟨10.1007/s11663-021-02352-x⟩. ⟨hal-03437449⟩
57 Consultations
244 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More