Calage inverse d'un modèle d'endommagement sur des essais de fatigue en flexion
Résumé
Laboratory fatigue tests allow us to characterize the fatigue behaviour and to study the cyclic damage of bituminous materials. It is well known that the specimen shape influence the global response of fatigue tests. In order to reach an intrinsic characterization, a fatigue damage model was developed to describe the loss of material stiffness during laboratory fatigue tests. Nevertheless, material parameters had to be fitted on data to use the model for predictions. An optimisation method based on the Levenberg-Marquardt algorithm is presented to fit numerical data on experimental data. Two categories of laboratory tests were considered in this study: tension compression and two-points bending test. This method allows us to identify the damage model regardless of the sample geometry.
Les essais de fatigue de laboratoire nous permettent de caractériser le comportement de fatigue et d'étudier l'endommagement cyclique des matériaux bitumineux. La géométrie de l'échantillon a une influence sur la réponse globale des essais de fatigue. Afin d'avoir une caractérisation intrinsèque, un modèle d'endommagement a été développé pour décrire la perte de raideur du matériau lors des essais de fatigue en laboratoire. Des paramètres matériau sont à identifier sur des données expérimentales. Une méthode d'optimisation, qui utilise l'algorithme de Levenberg-Marquardt, est présentée ici pour ajuster des données numériques sur des données expérimentales. Deux catégories d'essais sont utilisées : des essais de traction compression uniaxiaux et des essais de flexion sur poutre console trapézoïdale. La méthode nous permet d'identifier le modèle d'endommagement indépendamment de la géométrie d'échantillon.
Domaines
Mécanique [physics]
Origine : Fichiers éditeurs autorisés sur une archive ouverte