Investigation of Mn Promotion on HKUST‐1 Metal‐Organic Frameworks for Low‐Temperature Selective Catalytic Reduction of NO with NH 3 - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue ChemCatChem Année : 2021

Investigation of Mn Promotion on HKUST‐1 Metal‐Organic Frameworks for Low‐Temperature Selective Catalytic Reduction of NO with NH 3

Résumé

A series of HKUST-1 supported catalysts (also known as Cu-BTC, or MOF-199 [copper(II)-benzene-1,3,5-tricarboxylate]) modified with different loadings of managanese were synthesized and characterized by powder X-ray diffraction, scanning electron microscopy/energy dispersive spectroscopy, nitrogen sorption, thermogravimetric analysis, and temperature-programmed desorption with NH3. The structural and textural properties of the solids compared to the reference support are preserved as much as possible when the manganese content is not higher than 5 wt.%. This makes it possible to obtain effective catalysts at low temperatures (<200°C) in the selective catalytic reduction of NO with NH3, since high specific surface area is well-retained. Higher efficiency is obtained with the catalyst containing 3.75 wt.% of manganese which exhibits NO conversion of 68% at Weight Hourly Space Velocity (WHSV) of 96,000 ml/h·g. This performance in NO reduction is recognized to be one of the best in the series of HKUST-1-Mnx catalysts. Nevertheless, their narrow temperature window for the working reaction and sensitivity to the presence of water vapor and sulfur dioxide remain a drawback.

Domaines

Catalyse
Fichier principal
Vignette du fichier
Swirk ChemCatChem2021.pdf (1.47 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03351240 , version 1 (22-09-2021)

Identifiants

Citer

Katarzyna Świrk, Gérard Delahay, Abdelali Zaki, Karim Adil, Amandine Cadiau. Investigation of Mn Promotion on HKUST‐1 Metal‐Organic Frameworks for Low‐Temperature Selective Catalytic Reduction of NO with NH 3. ChemCatChem, 2021, 13 (18), pp.4029-4037. ⟨10.1002/cctc.202100431⟩. ⟨hal-03351240⟩
40 Consultations
97 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More