Recovery of severely deformed ferrite studied by in situ high energy X-ray diffraction

Résumé

Highlights :  Recovery of severely deformed ferrite was followed in situ by High Energy X Ray Diffraction during heating and isothermal holding experiments.  Dislocation densities during annealing were determined by a modified Williamson Hall method.  A saturation in recovery has been observed in all studied conditions whatever the holding temperature.  The beginning of recrystallization is detected by a large density drop at 650 °C.

Domaines

Fichier principal
Vignette du fichier
couchet2021material-characterization.pdf (1.44 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)
Licence

Dates et versions

hal-03325592 , version 1 (25-08-2021)

Licence

Identifiants

Citer

Clélia Couchet, Sébastien y P Allain, Guillaume Geandier, Julien Teixeira, Steve Gaudez, et al.. Recovery of severely deformed ferrite studied by in situ high energy X-ray diffraction. Materials Characterization, 2021, 179, pp.111378. ⟨10.1016/j.matchar.2021.111378⟩. ⟨hal-03325592⟩
175 Consultations
396 Téléchargements

Altmetric

Partager

  • More