Evaluation Of Mechanical, Biodegradable & Microstructure Analysis of Epoxy-Based Glass, Carbon and Jute Fiber Reinforced Bio-Composites Used as Orthopedic Implants [Human Bone]

Résumé

The aim of the present research work is experimental investigation to evaluate various physical, Mechanical and Corrosion Test Properties and concentrates on the progress of biomaterials in the field of orthopedics especially for Tibia bone an effort to utilize the 10% JPCM(S1), 10% EPCM(S2) and 10% CPCM(S3), and fabricated the bio composites materials. The present invention focuses on the enhanced properties of 10% JPCM(S1), 10% EPCM(S2) and 10% CPCM(S3) as Tibia bone implant material. It is a challenge to the creation of better materials for the improvement of quality of life and Economical one suggests to use Tibia Bone Prosthesis (Rods, Plates etc.,) and also Characterization is carried out using Epoxy resin-LY556 as a matrix material and hardener-HY 951 with 10% Carbon fiber, E-Glass fiber and Jute fiber reinforced composite material with 0+/-90 Degree orientation. by using hand layup fabrication technique the specimens are prepared as per biomaterials ASTM standards for Tensile Tests specimens are prepared by ASTM D-3039, For Compression Tests specimens are prepared by ASTM D-3410 and for Bending Tests specimens are prepared by ASTM D-790 , Wear by G-99, Fatigue test was conducted i.e. ASTM D3479 / D3479M-19 and ASTM D-3039 Standard also Moisture ,Impact and Corrosion test was also carried out according to ISO standard for the same specimen to know the biocompatibility.
Fichier principal
Vignette du fichier
Article 3.pdf (1.51 Mo) Télécharger le fichier
Origine Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-03284138 , version 1 (23-07-2021)

Identifiants

  • HAL Id : hal-03284138 , version 1

Citer

Shivanand N. Pujar, K. R. Dinesh, Jagdish S.P, Shiva Kumar Gouda. Evaluation Of Mechanical, Biodegradable & Microstructure Analysis of Epoxy-Based Glass, Carbon and Jute Fiber Reinforced Bio-Composites Used as Orthopedic Implants [Human Bone]. Journal of Scholastic Engineering Science and Management, 2021, 1 (3), pp.32-47. ⟨hal-03284138⟩
89 Consultations
46 Téléchargements

Partager

Gmail Mastodon Facebook X LinkedIn More