Correlation between TEM, SAXS and DSC to investigate the influence of SPD on precipitation mechanisms of an Al-Zn-Mg-Cu alloy

Résumé

This study allowed to understand the influence of severe plastic deformation by High Pressure Torsion (HPT) on an Al-Zn-Mg-Cu alloy and more especially the influence on precipitation mechanisms thanks to the correlation between DSC, SAXS and STEM data. A shear strain of γ ≈ 200 was first applied to the alloy. This deformation leads to nanostructuration, creation of high density of defects but also solute segregation to boundaries and dynamic precipitation. These specific microstructural features give rise to an acceleration of precipitation kinetics during heat treatments but also to a lower precipitation temperature and a modification of final precipitates size distribution as compared to the un-deformed alloy.
Fichier principal
Vignette du fichier
Duchaussoy et al. - 2020 - Correlation between TEM, SAXS and DSC to investiga.pdf (2.09 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte
Loading...

Dates et versions

hal-02990638 , version 1 (05-11-2020)

Identifiants

Citer

Amandine Duchaussoy, Alexis Deschamps, Xavier Sauvage, Frédéric de Geuser, Zenji Horita. Correlation between TEM, SAXS and DSC to investigate the influence of SPD on precipitation mechanisms of an Al-Zn-Mg-Cu alloy. MATEC Web of Conferences, 2020, 326, ⟨10.1051/matecconf/202032608006⟩. ⟨hal-02990638⟩
39 Consultations
52 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More