Stable single domain Co nanodisks: synthesis, structure and magnetism

Résumé

Colloidal synthesis of morphologically stable oxide-free cobalt nanodisks (diameter ≈ 21 nm, thickness ≈ 12 nm) has been achieved. The hcp c-axis is found to be perpendicular to the flat side of the disk which is explained by surface energy considerations. Magnetic measurements and comparisons with simulations show that the nanodisks are single magnetic domains with a magnetisation oriented perpendicular to the plane of the disks and reaching that of bulk cobalt, and high anisotropy field. These disks are thus potential candidates for magnetic data storage, magnetic sensor arrays, and cheap permanent magnets.

Fichier principal
Vignette du fichier
HAL version.pdf (1007.97 Ko) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)
Licence

Dates et versions

hal-02909554 , version 1 (30-09-2024)

Licence

Identifiants

Citer

Miguel Comesaña-Hermo, Diana Ciuculescu-Pradines, Zi-An Li, Sven Stienen, Marina Spasova, et al.. Stable single domain Co nanodisks: synthesis, structure and magnetism. Journal of Materials Chemistry, 2012, 22 (16), pp.8043. ⟨10.1039/C2JM16751D⟩. ⟨hal-02909554⟩
205 Consultations
73 Téléchargements

Altmetric

Partager

  • More