Moiré Structure of the 2-Mercaptobenzothiazole Corrosion Inhibitor Adsorbed on a (111)-Oriented Copper Surface

Résumé

The adsorption of 2-mercaptobenzothiazole (2-MBT) vapor on a Cu(111) surface under ultra-low pressure was investigated. For an exposure of 45 L at 150°C, a Moiré pattern was observed as a result of the superposition of an underlying (SQRT3xSQRT3)R30°structure and an outer layer compressed by 18% and rotated by 1.2°. The Moiré pattern was rich in S bonded to Cu as a result of molecular decomposition and partial desorption and was transformed to a (SQRT7×SQRT7)R19.1°structure when the sample temperature was increased above 250°C during deposition. This pre-adsorbed Moiréstructure led to the sharp decrease of the oxidation kinetics, which better protects copper against corrosion than the non-ordered 2-MBT monolayer formed at room temperature. Upon further exposure to 2-MBT at room temperature, an equivalent monolayer of the molecule was adsorbed on the Moiré structure at saturation whereas a multilayer was formed for the direct deposition on Cu(111) at room temperature.

Fichier principal
Vignette du fichier
CIMNAS Article 19_Final printed version.pdf (7.57 Mo) Télécharger le fichier
Origine Fichiers éditeurs autorisés sur une archive ouverte
Licence
Loading...

Dates et versions

hal-02906111 , version 1 (24-07-2020)

Licence

Identifiants

Citer

Xiaocui Wu, Frédéric Wiame, Vincent Maurice, Philippe Marcus. Moiré Structure of the 2-Mercaptobenzothiazole Corrosion Inhibitor Adsorbed on a (111)-Oriented Copper Surface. Journal of Physical Chemistry C, 2020, 124 (29), pp.15995-16001. ⟨10.1021/acs.jpcc.0c04083⟩. ⟨hal-02906111⟩
81 Consultations
123 Téléchargements

Altmetric

Partager

  • More