Behavior in oxidation at elevated temperature of {25Cr, 0.4C-6Ta}-containing Ni and Co-based cast alloys versus their proportion in nickel and cobalt - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Materials and Corrosion / Werkstoffe und Korrosion Année : 2018

Behavior in oxidation at elevated temperature of {25Cr, 0.4C-6Ta}-containing Ni and Co-based cast alloys versus their proportion in nickel and cobalt

Patrice Berthod
Zohra Himeur
  • Fonction : Auteur
  • PersonId : 1050799

Résumé

A series of six alloys from Ni-25Cr-0.4C-6Ta to Co-25Cr-0.4C-6Ta with a progressive addition of Co in substitution to Ni were elaborated. They were tested for 24 hours at 1237°C in laboratory air. The corrosion products formed around the samples and the deterioration of the subsurface were analyzed to characterize the high temperature oxidation behavior of these alloys. Three of the studied alloys, the nickel-richest ones, well behaved until 24 hours at this temperature. Their external oxide scales were essentially composed of chromia. In contrast, locally, the three cobalt-richest alloys were starting to oxidize catastrophically. The significant worsening of the oxidation behavior from the 27wt.%Co-containing alloy to the 41wt.%Co-containing one suggests that a critical Co content exists between these two values.
Fichier principal
Vignette du fichier
MaterialsAndCorrosion2018vol69p703.pdf (608.74 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02863248 , version 1 (10-06-2020)

Identifiants

Citer

Patrice Berthod, Zohra Himeur. Behavior in oxidation at elevated temperature of {25Cr, 0.4C-6Ta}-containing Ni and Co-based cast alloys versus their proportion in nickel and cobalt. Materials and Corrosion / Werkstoffe und Korrosion, 2018, 69 (6), pp.703-713. ⟨10.1002/maco.201709820⟩. ⟨hal-02863248⟩
80 Consultations
59 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More