Long-term seawater ageing effect on fatigue crack growth of CFRP for marine propellers
Effet du vieillissement à long terme d’un composite carbone époxy sur la fatigue en fissuration pour application pâle d’hélice
Résumé
This paper describes the influence of long-termimmersion in seawater on the crack propagation behavior in composites. The composite studied is an epoxy resin reinforced by continuous carbon fibres. Crack propagation tests were performed under mode I and mode II static and cyclic loading. Seawater diffusion into this material was found to be Fickian and tests were carried out on specimens unaged, seawater saturated, and dried after saturation. Saturated mode I and mode II specimens lose fracture resistance. However, after drying mode II fracture energy is recovered,while losses measured under mode I loading are permanent.
Cette article présente l’effet du vieillissement à long terme en eau de mer sur les propriétés en fatigue en fissuration d’un composite. Ce matériau composite est composé d’une résine époxy et d’un renfort fibre longues en carbone. Les essais de fissuration en fatigue ontété effectués suivant le mode I et le mode II. Des vieillissements en eau de mer ont montré un comportement Fickien et les éprouvettes de fatigue ont donc été testées en condition non vieilli et à saturation.Les résultats indiquent une dégradation des propriétés après saturation. Par contre, en mode I cette réduction est permanente, tandis qu’en mode II elle est réversible.
| Origine | Fichiers produits par l'(les) auteur(s) |
|---|
Loading...