Experimental and Thermodynamic Study of Nickel-Base Alloys containing Chromium Carbides: Part II -Study of the Sub-Surface Characteristics of Ni-30%wt.Cr-xC Alloys oxidized at High Temperature using Thermodynamic Calculations - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Calphad Année : 2008

Experimental and Thermodynamic Study of Nickel-Base Alloys containing Chromium Carbides: Part II -Study of the Sub-Surface Characteristics of Ni-30%wt.Cr-xC Alloys oxidized at High Temperature using Thermodynamic Calculations

P. Berthod

Résumé

Six ternary Ni-30 wt.%Cr-xC alloys (x = 0.2 to 2.0) were oxidized at 1,000, 1,100 and 1,200°C. For several of them, the sub-surface was studied with accuracy by division into several successive parts for local measurements of carbide fractions by image analysis. Additionally thermodynamic calculations were performed for local analysis of the samples. By these means, the outer carbide-free zone and the inner zone enriched in carbides were characterized, with special attention to both local carbon contents and local solidus temperatures. Profiles of carbon contents (and thereafter of local solidus temperatures) across the zone affected by oxidation were obtained by thermodynamic calculations. The content of carbon still present in the carbide-free zone is necessarily very low. The carbon content in the zone enriched in carbides is higher than in the bulk. The loss of carbon leads to a higher refractoriness for the carbide-free zone, which could protect the bulk against fast oxidation if it becomes partially molten because of a sudden increase in temperature in service.
Fichier principal
Vignette du fichier
Calphad2008p492.pdf (805.27 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02423323 , version 1 (23-12-2019)

Identifiants

Citer

P. Berthod. Experimental and Thermodynamic Study of Nickel-Base Alloys containing Chromium Carbides: Part II -Study of the Sub-Surface Characteristics of Ni-30%wt.Cr-xC Alloys oxidized at High Temperature using Thermodynamic Calculations. Calphad, 2008, ⟨10.1016/j.calphad.2008.06.005⟩. ⟨hal-02423323⟩
14 Consultations
58 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More