New Process for High Rate Production of Composite Parts based on Thermoplastics (INCREASE Project)
Nouveau Procédé pour la Fabrication Haute Cadence de Pièces Composites base Thermoplastiques (Projet INCREASE)
Résumé
A new direct process for the production of thermoplastic-based composite parts is proposed (C-RTM TP): injection in a partially closed hot mold containing the preformed dry reinforcement (3D preform), and controlled closure of the mold controlled in speed or force . The polymers used (amorphous or semi-crystalline) have a viscosity of between 25 and 75 Pa.s at Tf + 25 ° C. NCF reinforcements with a specific sewing thread compatible with the processing temperatures (up to 400 ° C) have been developed. A manufacturing pilot was set up around a bi-material horizontal electric press (600t) and a mold (400 °C) with 2 stations (impregnation / injection): INCREASE project.
Un nouveau procédé direct pour la production de pièces composites à base thermoplastique est proposé (C-RTM TP) : injection dans un moule chaud partiellement fermé contenant le renfort sec préformé (préforme 3D), et fermeture contrôlée du moule pilotée en vitesse ou en effort. Les polymères utilisés (amorphes ou semi-cristallins) présentent une viscosité entre 25 et 75 Pa.s à Tf + 25°C. Des renforts NCF avec un fil de couture spécifique compatibles avec les températures de mise en œuvre (jusqu’à 400°C) ont été développés.Un pilote de fabrication a été mis en place autour d’une presse horizontale électrique bi matière (600t) et d’un moule (400°C) à 2 postes (imprégnation/injection): projet INCREASE.
| Format | Poster |
|---|
Loading...