Formation of crystallographically oriented metastable Mg$_{1.8}$Si in Mg ion-implanted Si - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Cryst.Growth Des. Année : 2019

Formation of crystallographically oriented metastable Mg$_{1.8}$Si in Mg ion-implanted Si

Résumé

Metastable hexagonal Mg–Si was synthesized by implanting Mg ion into Si. Single-crystalline Si(111) was irradiated with Mg ions at elevated temperature followed by thermal annealing under vacuum. Microstructural analysis with transmission electron microscopy revealed the formation of precipitates with sizes of several 10 nm in the damaged crystalline Si matrix. Using electron diffraction, the precipitates were identified as Mg1.8Si, and the crystallographic orientation relationship between Mg1.8Si precipitates and Si was determined. The phase stability of Mg1.8Si in the Si matrix is discussed in terms of the internal stress generated during the precipitation process.
Fichier principal
Vignette du fichier
2019 Kobayashi Naito_HAL_Cryst Gowth Des19_7138_Mg in Si.pdf (2.12 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-02350393 , version 1 (24-08-2021)

Identifiants

Citer

Yuki Kobayashi, Muneyuki Naito, Koichi Sudoh, Aurélie Gentils, Cyril Bachelet, et al.. Formation of crystallographically oriented metastable Mg$_{1.8}$Si in Mg ion-implanted Si. Cryst.Growth Des., 2019, pp.acs.cgd.9b01002. ⟨10.1021/acs.cgd.9b01002⟩. ⟨hal-02350393⟩
27 Consultations
48 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More