One-pot synthesis of tailored Pd-Co nanoalloy particles confined in mesoporous carbon - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Microporous and Mesoporous Materials Année : 2016

One-pot synthesis of tailored Pd-Co nanoalloy particles confined in mesoporous carbon

A. Puscasu
  • Fonction : Auteur
A. M. de Yuso
  • Fonction : Auteur
C. Zlotea
Y. Oumellal
  • Fonction : Auteur
M. Latroche
Cathie Vix
  • Fonction : Auteur
  • PersonId : 1052922

Résumé

The synthesis of mesoporous carbon with confined PdCo nanoalloy particles by a one-pot soft-template approach is reported herein. The influence of metal precursor type, metal composition and annealing temperature on the carbon@PdCo material characteristics was systematically investigated. Small and homogeneously distributed PdCo nanoparticles in the carbon matrix were achieved. The PdCo particle size could be tuned from 8 to 25 nm and the metal composition proved to be the main parameter controlling the size. When the amount of Pd is low (Pd50Co50) the particle is small and increases with the increase of temperature. On the contrary, for richer Pd contents (Pd75Co25, Pd90Co10) the particle size is larger but they exhibit extremely high stability with no obvious modification of size between 450 and 800 °C. The tuned experimental parameters had less impact on the materials textural characteristics, they exhibit similar surface area and uniform pore size distribution. Among the materials, only the Pd rich alloys (Pd90Co10) are able to form metallic hydride and consequently, showing the highest hydrogen adsorption capacity.

Domaines

Matériaux
Fichier non déposé

Dates et versions

hal-02272645 , version 1 (27-08-2019)

Identifiants

Citer

Camelia Ghimbeu, A. Puscasu, A. M. de Yuso, C. Zlotea, Y. Oumellal, et al.. One-pot synthesis of tailored Pd-Co nanoalloy particles confined in mesoporous carbon. Microporous and Mesoporous Materials, 2016, 223, pp.79-88. ⟨10.1016/j.micromeso.2015.10.031⟩. ⟨hal-02272645⟩
20 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More