Light-induced defect states in hydrogenated amorphous silicon centered around 1.0 and 1.2 eV from the conduction band edge

J. Deng
  • Fonction : Auteur
R. W Collins
  • Fonction : Auteur
C R Wronski
  • Fonction : Auteur

Résumé

To take into account the presence of multiple light-induced defect states in hydrogenated amorphous silicon (a-Si:H) the evolution of the entire spectra of photoconductive subgap absorption, (h), has been analyzed. Using this approach two distinctly different light-induced defect states centered around 1.0 and 1.2 eV from the conduction band edge are clearly identified. Results are presented on their evolution and respective effects on carrier recombination that clearly point to the importance of these states in evaluating the stability of different a-Si:H solar cell materials, as well as elucidating the origin of the Staebler-Wronski effect.

Fichier principal
Vignette du fichier
Light-induced_defect_states_in_hydrogena.pdf (54.69 Ko) Télécharger le fichier
Origine Fichiers éditeurs autorisés sur une archive ouverte
Licence
Loading...

Dates et versions

hal-02119517 , version 1 (03-05-2019)

Licence

Identifiants

Citer

J. M Pearce, J. Deng, R. W Collins, C R Wronski. Light-induced defect states in hydrogenated amorphous silicon centered around 1.0 and 1.2 eV from the conduction band edge. Applied Physics Letters, 2003, 83 (18), pp.3725-3727. ⟨10.1063/1.1624637⟩. ⟨hal-02119517⟩
24 Consultations
153 Téléchargements

Altmetric

Partager

  • More