STEM-EELS identification of TiOXNY, TiN, Ti2N and O, N dissolution in the Ti2642S alloy oxidized in synthetic air at 650 °C - Archive ouverte HAL Access content directly
Journal Articles Corrosion Science Year : 2019

STEM-EELS identification of TiOXNY, TiN, Ti2N and O, N dissolution in the Ti2642S alloy oxidized in synthetic air at 650 °C

Abstract

Oxide-alloy interface of Ti6242S Ti-based alloy was investigated by STEM-EELS technique, after oxidation in both N2-free and synthetic air atmospheres at 650 °C for 1000 h. The chemical shift of Ti-L2,3 edge and its specific fine structure along the oxide-alloy interface were used as fingerprint to distinguish the different compositions of titanium nitrides and oxynitrides. TiN, Ti2N and TiNxOy were identified in the sample oxidized in synthetic air at the oxide-alloy interface. Moreover, a decreasing in the oxidation state of Ti oxides was found along with Sn segregation at the oxide-alloy interface for the sample oxidized in N2-free atmosphere.

Domains

Materials
Fichier principal
Vignette du fichier
Abdallah_23796.pdf (10.33 Mo) Télécharger le fichier
Origin : Files produced by the author(s)
Loading...

Dates and versions

hal-02115253 , version 1 (30-04-2019)

Identifiers

Cite

Iman Abdallah, Charlotte Dupressoire, Lydia Laffont, Daniel Monceau, Aurélie Vande Put. STEM-EELS identification of TiOXNY, TiN, Ti2N and O, N dissolution in the Ti2642S alloy oxidized in synthetic air at 650 °C. Corrosion Science, 2019, 153, pp.191-199. ⟨10.1016/j.corsci.2019.03.037⟩. ⟨hal-02115253⟩
49 View
78 Download

Altmetric

Share

Gmail Facebook X LinkedIn More