Synthesis, crystallographic structure and thermodynamic properties of T2-Al2MgC2

Résumé

Grain refinement of Mg–Al based alloys is challenging because it is known that Zr, which is extremely effective in many Al-free alloys, cannot be used. The addition of carbon through various routes by using carbon-containing sources is considered as an option. The grain refinement mechanisms are still under debate. The present work is focused on the ternary base system Mg–Al–C, including the potential nucleants Al4C3 and Al2MgC2, presently without consideration of Al2CO. The ternary carbide Al2MgC2 was synthesized and characterized using sealed Ta crucibles. The decomposition of the carbide was measured at 1290 °C by Differential Thermal Analysis under a pressure of 8 bar. Practical difficulties, including high vapor pressure of Mg and high affinity of Mg with oxygen, as well as rapid hydrolysis of the Al2MgC2 carbide have been overcome.
Fichier principal
Vignette du fichier
T2Def20_T2-Al2MgC2_HAL.pdf (1.42 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-02062499 , version 1 (02-12-2020)

Identifiants

Citer

Guillaume Deffrennes, Bruno Gardiola, Erwann Jeanneau, Georges Mikaelian, Benigni P., et al.. Synthesis, crystallographic structure and thermodynamic properties of T2-Al2MgC2. Journal of Solid State Chemistry, 2019, 273, pp.150-157. ⟨10.1016/j.jssc.2019.02.039⟩. ⟨hal-02062499⟩
168 Consultations
101 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More