Large magnetocaloric effect in manganese perovskite La 0.67−x Bi x Ba 0.33 MnO 3 near room temperature

Résumé

La0.67−xBixBa0.33MnO3 (x = 0 and 0.05) ceramics were prepared via the sol–gel method. Structural, magnetic and magnetocaloric effects have been systematically studied. X-ray diffraction shows that all the compounds crystallize in the rhombohedral structure with the R[3 with combining macron]c space group. By analyzing the field and temperature dependence of magnetization, it is observed that both samples undergo a second order magnetic phase transition near TC. The value of TC decreases from 340 K to 306 K when increasing x from 0.00 to 0.05, respectively. The reported magnetic entropy change for both samples was considerably remarkable and equal to 5.8 J kg−1 K−1 for x = 0.00 and 7.3 J kg−1 K−1 for x = 0.05, respectively, for μ0H = 5 T, confirming that these materials are promising candidates for magnetic refrigeration applications. The mean-field theory was used to study the magnetocaloric effect within the thermodynamics of the model. Satisfactory agreement between experimental data and the mean-field theory has been found.

Domaines

Matériaux
Fichier principal
Vignette du fichier
c8ra09802.pdf (1.46 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-02024089 , version 1 (10-07-2023)

Identifiants

Citer

Ah. Dhahri, E. Dhahri, E.K. Hlil. Large magnetocaloric effect in manganese perovskite La 0.67−x Bi x Ba 0.33 MnO 3 near room temperature. RSC Advances, 2019, 9 (10), pp.5530-5539. ⟨10.1039/C8RA09802F⟩. ⟨hal-02024089⟩

Collections

UGA CNRS NEEL
17 Consultations
6 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More