Caractérisation expérimentale des propriétés chimio-mécaniques de l'interphase pâte de ciment-granulat par MEB et nano-indentation
Résumé
This article presents an experimental study of the chemical and mechanical properties of the interphase cement paste / aggregate. The interphase zone is the zone of the cement paste which is in the immediate vicinity of the aggregate to a thickness of about 20-50 μm and which has different mechanical and chemical properties compared to the pure cement paste. Cement paste / limestone aggregate composite samples were fabricated to allow the study of the chemical and mechanical properties of the interphase. The cement paste is made of Portland cement with an W / C ratio of 0.4. Calcium concentration profiles around the interphase area show a high concentration of calcium due to the presence of portlandite. The nano-indentation tests indicate a zone of weakness at the interphase level.
Cet article présente une étude expérimentale des propriétés chimiques et mécaniques de l'interphase pâte de ciment / granulat. La zone d'interphase est la zone de la pâte de ciment qui se trouve à proximité immédiate du granulat sur une épaisseur d'environ 20-50 µm et qui possède des propriétés mécaniques et chimiques différentes de celles de la pâte de ciment pure. Des échantillons composites pâte de ciment / granulat calcaire ont été conçus et préparés afin de permettre l'étude des propriétés chimiques et mécaniques de l'interphase. La pâte de ciment est réalisée à base de ciment Portland avec un rapport E/C de 0,4. Les profils de concentration en Calcium réalisés autour la zone de l'interphase montrent une forte concentration en calcium due à la présence de la portlandite. Les essais de nano-indentation indiquent une zone de faiblesse au niveau de l'interphase.
| Origine | Fichiers produits par l'(les) auteur(s) |
|---|