TEM investigation of iron segregation modes in CuAlFe dilute alloys

Résumé

Iron has a very low solubility in copper (a few % at 1000 °C) as well as in the α solid solution of the Cu-Al alloy. We describe here the iron segregation modes which are observed during the slow cooling of the α (FCC) and β (BCC) solid solutions of CuAlFe alloys containing about 10 wt% Al and 4% Fe. At high temperature iron at first precipitates into α or r Fe; then at lower temperature iron-rich phases are observed containing also Cu and Al. Particularly, the α2 phase appears very quickly, and it is thought to be richer in Fe than the α matrix.
La solubilité du fer dans le cuivre est très faible (quelques % à 1000 °C), et on sait qu'elle demeure faible dans la solution solide α de cuivre aluminium. Nous décrivons ici les modes de ségrégation du fer observés au cours du refroidissement lent des solutions solides α (CFC) et β (CC) d'alliages ternaires CuAlFe de teneurs en Al proches de 10% mass. et contenant 4% Fe. A haute température, le fer a d'abord tendance à ségréger en fer α ou en fer r ; lorsque la température diminue, on observe la précipitation de phases riches en fer, mais contenant aussi du cuivre et de l'aluminium. Nous montrons en particulier que la phase stable α 2 se forme trés vite, et nous pensons qu'elle est plus riche en fer que la matrice α.

Dates et versions

hal-01928969 , version 1 (20-11-2018)

Identifiants

Citer

Annie Hauet, A. Bigot, D. Blavette. TEM investigation of iron segregation modes in CuAlFe dilute alloys. Microscopy, Microanalysis, Microstructures, 1994, 5 (3), pp.203--211. ⟨10.1051/mmm:0199400503020300⟩. ⟨hal-01928969⟩
27 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More