Influence of the initial Li/Co ration in LiCoO2 on the high-voltage phase-transition mechanisms

Résumé

The influence of the initial Li/Co stoichiometry in LiCoO2 (LCO) (1.00 ≤ Li/Co ≤ 1.05) on the phase-transition mechanisms occurring at high voltage during lithium deintercalation (V > 4.5 vs Li+/Li) was investigated by in situ X-ray diffraction. Even if the excess Li+ in Li1.024Co0.976O1.976 does not hinder the formation of the H1–3 and O1 phases, the latter are obtained at higher voltages and exhibit larger c parameters compared with their analogues formed from Li1.00CoO2. We also showed that for the stoichiometric Li1.00CoO2 the deintercalation process is more complex than already reported, with the formation of an intermediate structure between H1–3 and O1.

Domaines

Fichier principal
Vignette du fichier
2018-146.pdf (1.26 Mo) Télécharger le fichier
2018-146-SI.pdf (1.23 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)
Licence

Dates et versions

hal-01885180 , version 1 (01-10-2018)

Licence

Identifiants

Citer

Marie Duffiet, Maxime Blangero, Pierre-Etienne Cabelguen, Claude Delmas, Dany Carlier. Influence of the initial Li/Co ration in LiCoO2 on the high-voltage phase-transition mechanisms. Journal of Physical Chemistry Letters, 2018, 9 (18), pp.5334-5338. ⟨10.1021/acs.jpclett.8b02252⟩. ⟨hal-01885180⟩
141 Consultations
781 Téléchargements

Altmetric

Partager

  • More