Rietveld refinements, impedance spectroscopy and phase transition of the polycrystalline ZnMoO4 ceramics - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Ceramics International Année : 2015

Rietveld refinements, impedance spectroscopy and phase transition of the polycrystalline ZnMoO4 ceramics

Résumé

The triclinic phase of zinc molybdate ?-ZnMoO 4 (ZMO) was synthesized by a simple co-precipitation method at 600°C. The crystal structure of the obtained polycrystalline sample of ZMO was characterized by X-ray diffraction (XRD) and Rietveld calculations using the space group P-1. The electrical properties of ?-ZnMoO 4 compacted pellets were determined at room temperature from Electrical Impedance Spectrometry (EIS), in the temperature range of 400°C to 700°C. Nyquist representations were interpreted in terms of two types of electrical circuits, involving a high frequency bulk component and a low frequency Warburg component. Analyses of the frequency dependence of the real and imaginary impedance show a non-debye type relaxation. A phase transition corresponding to the allotropic transformation triclinic-monoclinic (α?β) of ZnMoO 4 was observed in the temperature range of 450 to 500°C, with a variation of activation energies. The Warburg component is discussed in terms of electrode surface reactions.
Fichier principal
Vignette du fichier
aitahsaine2015-1.pdf (729.18 Ko) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-01872783 , version 1 (15-06-2021)

Licence

Identifiants

Citer

H. Ait Ahsaine, M. Zbair, M. Ezahri, A. Benlhachemi, Madjid Arab, et al.. Rietveld refinements, impedance spectroscopy and phase transition of the polycrystalline ZnMoO4 ceramics. Ceramics International, 2015, 41 (10), pp.15193-15201. ⟨10.1016/j.ceramint.2015.08.094⟩. ⟨hal-01872783⟩
132 Consultations
163 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More