Structural, vibrational study and UV photoluminescence properties of the system Bi<sub>(2−x)</sub>Lu<sub>(x)</sub>WO<sub>6</sub> (0.1≤x≤1) - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue RSC Advances Année : 2015

Structural, vibrational study and UV photoluminescence properties of the system Bi(2−x)Lu(x)WO6 (0.1≤x≤1)

Résumé

The bismuth lutetium tungstate series Bi(2−x)Lu(x)WO6 with 0.1 ≤ x ≤ 1 were synthesized by solid state reaction of oxide precursors at 1000 °C for 3 h. The as-prepared polycrystalline compounds were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), Raman spectroscopy and photoluminescence (PL) analyses. Biphasic samples were obtained in the composition range of 0.1 ≤ x ≤ 0.3. Solid solutions were obtained in the composition range of 0.4 ≤ x ≤ 1, and their monoclinic crystal structure was refined using the Rietveld method. SEM micrographs showed that solid solutions presented homogeneous morphologies. Attributions of Raman vibrational modes were proposed. A shift in the vibrational wavenumber depending on the lutetium composition was observed. The specific broadening of the spectral bands was interpreted in terms of long range Bi/Lu disorder and local WO6 octahedron distortions in the structure. The PL experiments were performed under UV-laser light irradiation. Each PL band was decomposed into three Gaussian components with energies close to 1.25, 1.80 and 2.1 eV. Their integrated intensities increased with the value of x. The presence of the near infrared band at 1.25 eV is discussed.
Fichier principal
Vignette du fichier
aitahsaine2015.pdf (1.39 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-01872775 , version 1 (15-06-2021)

Licence

Paternité

Identifiants

Citer

H. Ait Ahsaine, M. Ezahri, A. Benlhachemi, B. Bakiz, Sylvie Villain, et al.. Structural, vibrational study and UV photoluminescence properties of the system Bi(2−x)Lu(x)WO6 (0.1≤x≤1). RSC Advances, 2015, 5 (116), pp.96242-96252. ⟨10.1039/C5RA19424E⟩. ⟨hal-01872775⟩
107 Consultations
55 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More