Comportement et durée de vie en fatigue isotherme de l'acier X 38 CrMoV 5

Résumé

Dies and molds are subjected to severe mechanical and thermal loads during injec tion or forging operations. As fatigue is one of the most important cause of tool steels damage, we studied isothermal (between 200°C and 600°C) fatigue behaviour and damage of two grades (SMV3 andADC3) of a tempered martensitic 5%Cr steel. More than 100fatigue tests were performed in order to analyse mechanical loading, temperature and initial hardness influences. We observed a softening during all lifetime which is typical of tempered martensitic steels. Softening amplitudes are increasing with increasing total strain amplitude, and decreasing with increasing temperature (till 550°C) and hardness (between 42 HRC and 50 HRC). Influences of temperature and hardness are limited when observed through a Manson-Coffin dia gram. Conversely, increasing test temperature or decreasing hardness leads to a strong reduction of lifetime (factor 1000 for a 8 HRC decrease!) when results are plotted in a Basquin diagram. Interrupted tests showed that crack initiation controls lifetime for a number of cycles to failure around 105cycles. Threesites ofcrack initiationwere identifiedanddiscussed:-non metallic inclusions (200°C-400°C) ;-lath boundary (200°C-400°C) ;-prior austenitic grain boundary (500°C-600°C).
Fichier principal
Vignette du fichier
Comportement_et_duree_de_vie_en_fatigue_isotherme.pdf (8.65 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01851452 , version 1 (06-11-2019)

Identifiants

Citer

Denis Delagnes, Farhad Rezai-Aria, Christophe Levaillant, André Grellier. Comportement et durée de vie en fatigue isotherme de l'acier X 38 CrMoV 5. Matériaux & Techniques, 1999, n°1-2, p. 39-50. ⟨10.1051/mattech/199987010039⟩. ⟨hal-01851452⟩
45 Consultations
153 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More