Structure dependent resistivity and dielectric characteristics of tantalum oxynitride thin films produced by magnetron sputtering - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Applied Surface Science Année : 2015

Structure dependent resistivity and dielectric characteristics of tantalum oxynitride thin films produced by magnetron sputtering

D. Cristea
  • Fonction : Auteur
A. Crisan
  • Fonction : Auteur
N. Cretu
  • Fonction : Auteur
J. Borges
  • Fonction : Auteur
V. Ion
  • Fonction : Auteur
M. Dinescu
  • Fonction : Auteur
N. P. Barradas
  • Fonction : Auteur
Daniela Munteanu

Résumé

The main purpose of this work is to present and to interpret the change of electrical properties of TaxNyOz thin films, produced by DC reactive magnetron sputtering. Some parameters were varied during deposition: the flow of the reactive gases mixture (N-2 and O-2, with a constant concentration ratio of 17:3); the substrate voltage bias (grounded, -50 V or -100 V) and the substrate (glass, (1 0 0) Si or high speed steel). The obtained films exhibit significant differences. The variation of the deposition parameters induces variations of the composition, microstructure and morphology. These differences cause variation of the electrical resistivity essentially correlated with the composition and structural changes. The gradual decrease of the Ta concentration in the films induces amorphization and causes a raise of the resistivity. The dielectric characteristics of some of the high resistance TaxNyOz films were obtained in the samples with a capacitor-like design (deposited onto high speed steel, with gold pads deposited on the dielectric TaxNyOz films). Some of these films exhibited dielectric constant values higher than those reported for other tantalum based dielectric films. (C) 2015 Elsevier B.V. All rights reserved.

Domaines

Matériaux
Fichier non déposé

Dates et versions

hal-01814295 , version 1 (13-06-2018)

Identifiants

Citer

D. Cristea, A. Crisan, N. Cretu, J. Borges, C. Lopes, et al.. Structure dependent resistivity and dielectric characteristics of tantalum oxynitride thin films produced by magnetron sputtering. Applied Surface Science, 2015, 354 (B), pp.298-305. ⟨10.1016/j.apsusc.2015.06.167⟩. ⟨hal-01814295⟩
32 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More