Elaboration and characterization of multiphase composites obtained by reaction sintering of boehmite and zircon - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Journal of The Australian Ceramic Society Année : 2014

Elaboration and characterization of multiphase composites obtained by reaction sintering of boehmite and zircon

H. Belhouchet
H. Makri
  • Fonction : Auteur
M. Hamidouche
  • Fonction : Auteur
N. Bouaouadja
  • Fonction : Auteur

Résumé

In this work, different composites (zircon-mullite-zirconia, mullite-zircon-zirconia, mullite-zirconia, mullite-zirconia-alumina and alumina-mullite-zirconia) were developed by reaction sintering of boehmite (AlOOH) and zircon (ZrSiO4). Several mixtures were used by varying the boehmite content from 10 to 90 wt. %. All powders were mixed and grounded by ball milling and then pressed in cylindrical form. Finally, the green specimens were sintered under normal conditions for 2 hours at temperatures between 1400 and 1600° C, with a heating rate of 5°C/min. The dilatometric curves reveal several microstructural transformations in these mixtures. The X-rays diffraction spectra revealed factors such as percentage of boehmite and zircon and the sintering temperature lead to the formation of several composites. The presence of the various phases was confirmed by micrographic observations. © 2014, Australasian Ceramic Society. All rights reserved.
Fichier non déposé

Dates et versions

hal-01808030 , version 1 (05-06-2018)

Identifiants

  • HAL Id : hal-01808030 , version 1

Citer

H. Belhouchet, H. Makri, M. Hamidouche, N. Bouaouadja, V. Garnier, et al.. Elaboration and characterization of multiphase composites obtained by reaction sintering of boehmite and zircon. Journal of The Australian Ceramic Society, 2014, 50 (2), pp.135-146. ⟨hal-01808030⟩
38 Consultations
0 Téléchargements

Partager

Gmail Facebook X LinkedIn More