Evaluation of multiple stress corrosion crack interactions by in-situ Digital Image Correlation

Résumé

Digital Image Correlation (DIC), Acoustic Emission and Electrochemical Noise measurements were applied to study the growth of multiple intergranular cracks as a colony on an Alloy 600 in a tetrathionate solution. Cracks exceeding 55 μm in length and 0.45 μm in opening were successfully detected by DIC. Moreover, crack population was classified into initiating, active and dormant cracks, active population being the larger one. The emergence and intensification of interactions produced a modification on the colony growth behavior. They range from a mostly surface crack propagation (in the absence of interactions), to in depth propagation predominantly governed by crack shielding.
Fichier principal
Vignette du fichier
bolivar2017.pdf (510.41 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-01804252 , version 1 (06-04-2021)

Licence

Paternité

Identifiants

Citer

J. Bolivar, Marion Fregonese, Julien Réthoré, C. Duret-Thual, P. Combrade. Evaluation of multiple stress corrosion crack interactions by in-situ Digital Image Correlation. Corrosion Science, 2017, 128, pp.120-129. ⟨10.1016/j.corsci.2017.09.001⟩. ⟨hal-01804252⟩
76 Consultations
208 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More