Domain wall motion in Pb(Zr$_{0.20}$Ti$_{0.80}$)O$_3$ epitaxial thin films

Résumé

Two Pb(ZrTi)O samples of different thickness and domain configuration have been studied. The c-domain sample was found to have a higher coercive field E and higher dielectric losses than the other which presents approximately 60% of c-domains and 40% of a-domains as observed by piezo force microscopy (PFM) characterization. Hyperbolic law measurements reveal that the higher coercive field is due to domain wall pinning in deeper defects and hence a higher field E is required for unpinning. The dissipation factors due to domain wall motion, however, are similar in both samples since the domain wall density is low and there is almost no interaction between domain walls. The higher dielectric losses in the c-domain oriented sample are a result of a greater contribution from the lattice and seem to be due to strain from the substrate, which is not relieved in a thin sample. PFM and dielectric characterization are complementary methods which provide a better understanding of the domain wall motion.
Fichier principal
Vignette du fichier
Borderon - Domain wall motion.pdf (2.16 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte
Loading...

Dates et versions

hal-01762561 , version 1 (27-06-2018)

Licence

Paternité

Identifiants

Citer

Caroline Borderon, Alan Brunier, Kevin Nadaud, Raphaël Renoud, Marin Alexe, et al.. Domain wall motion in Pb(Zr$_{0.20}$Ti$_{0.80}$)O$_3$ epitaxial thin films. Scientific Reports, 2017, 7 (1), pp.3444. ⟨10.1038/s41598-017-03757-y⟩. ⟨hal-01762561⟩
108 Consultations
56 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More