Microstructures and mechanical properties of a multi-phase β-solidifying TiAl alloy densified by spark plasma sintering

Résumé

This work deals with the densification of TNM alloys by spark plasma sintering. Pre-alloyed powders with composition Ti-43.9Al-4Nb-0.95Mo-0.1B (at.%) were sintered between 1237 and 1429 °C, applying a pressure of 100 MPa. The microstructures of the alloys were studied by scanning electron microscopy and transmission electron microscopy. Tensile tests at room temperature and creep experiments at 700 °C and 300 MPa stress were performed. Post-mortem analyses of deformed samples were also carried out by transmission electron microscopy to explain the mechanical properties. Duplex, nearly lamellar and so-called β microstructures were obtained as a function of the sintering temperature. Attention is focused on the nearly lamellar microstructure. This type of microstructure is composed of small lamellar α2/ γ-colonies, which are surrounded by γ + β0 intercolony borders. It exhibits very strong creep resistance associated with moderate ductility at room temperature. It is demonstrated that the use of β solidifying alloys during SPS is an efficient way to reduce the size of the lamellar microstructure. Finally, the mechanical properties obtained are explained in terms of the characteristics of this microstructure. © 2014 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Fichier non déposé

Dates et versions

hal-01726309 , version 1 (08-03-2018)

Identifiants

Citer

Thomas Voisin, Jean-Philippe Monchoux, Muriel Hantcherli, Svea Mayer, Helmut Clemens, et al.. Microstructures and mechanical properties of a multi-phase β-solidifying TiAl alloy densified by spark plasma sintering. Acta Materialia, 2014, 73, pp.107-115. ⟨10.1016/j.actamat.2014.03.058⟩. ⟨hal-01726309⟩
74 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More