Electrodeposition behavior, physicochemical properties and corrosion resistance of Ni-Co coating modified by gelatin additive

Résumé

The effect of gelatin on the microstructure, composition and electroplating mechanism of Ni–Co coating synthesized from sulfate media onto carbon steel substrate was investigated using AFM analysis, SEM/EDS and Electrochemical Quartz Crystal Microbalance (EQCM) coupled with chronopotentiometric measurements. The deposition of gelatin in the coating matrix was found to lower the mass of Ni–Co layers. Moreover, the adsorption of this additive seemed to inhibit the initial nucleation of the Ni–Co electrodeposition, showing homogeneous surface and smaller crystallites. Furthermore, the corrosion performance was studied in 3% NaCl solution by means of potentiodynamic polarization and electrochemical impedance spectroscopy (EIS). After a long immersion into chloride solution, Ni–Co–Gelatin (Ni–Co–Gel) coating showed a good stability and a better corrosion resistance. Therefore, the presence of gelatin additive impacted the crystal size, corrosion resistance and Ni–Co deposits morphology.

Domaines

Chimie
Fichier non déposé

Dates et versions

hal-01719694 , version 1 (28-02-2018)

Identifiants

Citer

I. Kharmachi, L. Dhouibi, P. Berçot, M. Rezrazi, B. Lakard. Electrodeposition behavior, physicochemical properties and corrosion resistance of Ni-Co coating modified by gelatin additive. Protection of Metals and Physical Chemistry of Surfaces, 2017, 53 (6), pp.1059-1069. ⟨10.1134/S2070205117060132⟩. ⟨hal-01719694⟩
41 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More