Origins of misorientation defects in single crystal castings: A time resolved in situ synchrotron X-ray radiography study - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue MATEC Web of Conferences Année : 2014

Origins of misorientation defects in single crystal castings: A time resolved in situ synchrotron X-ray radiography study

Résumé

The presence of grain boundaries in single crystal castings is intolerable owing to the detrimental impact on creep and fatigue behaviour. Whilst the origins of many defects such as freckles have been understood since the 1970s, other defects such as slivers, or indeed the small mosaicity observed in many castings have eluded comprehensive treatments. In the present work, in situ X-ray imaging has been used to examine the origin of misorientation defects that arise during solidification. Dendrite deformation was observed, which impacted growth characteristics and led to a permanent misoriention. Digital image correlation analysis showed the dendrites becoming increasingly bent as solidification progressed. In order to probe the deformation modes further, a method was devised to convert standard EBSD data into measurements of bending and torsion angle. It was demonstrated that such defects form as the result of bending moments arising from differential thermal contraction and gravity.

Domaines

Matériaux
Fichier principal
Vignette du fichier
matecconf_eurosuperalloys14_05003.pdf (855.68 Ko) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte
Licence : CC BY - Paternité

Dates et versions

hal-01708662 , version 1 (05-09-2023)

Licence

Paternité

Identifiants

Citer

J. Aveson, G. Reinhart, H. Nguyen-Thi, Nathalie Mangelinck-Noël, N. d'Souza, et al.. Origins of misorientation defects in single crystal castings: A time resolved in situ synchrotron X-ray radiography study. MATEC Web of Conferences, 2014, 14, pp.05003. ⟨10.1051/matecconf/20141405003⟩. ⟨hal-01708662⟩
99 Consultations
5 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More