Bis(formylphenolato)cobalt(II)-Mediated Alternating Radical Copolymerization of tert-Butyl 2-Trifluoromethylacrylate with Vinyl Acetate - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Polymers Année : 2017

Bis(formylphenolato)cobalt(II)-Mediated Alternating Radical Copolymerization of tert-Butyl 2-Trifluoromethylacrylate with Vinyl Acetate

Résumé

The organometallic-mediated radical polymerization (OMRP) of vinyl acetate (VAc) and its OMR copolymerization (OMRcoP) with tert-butyl 2-trifluoromethylacrylate (MAF-TBE) mediated by Co(SAL)2 (SAL = 2-formylphenolato or deprotonated salicylaldehyde) produced relatively well-defined PVAc and poly(VAc-alt-MAF-TBE) copolymers at moderate temperature (<40 °C) in bulk. The resulting alternating copolymer was characterized by 1H-, 13C- and 19F-nuclear magnetic resonance (NMR) spectroscopies, and by size exclusion chromatography. The linear first-order kinetic plot, the linear evolutions of the molar mass with total monomer conversion, and the relatively low dispersity (Đ~1.55) of the resulting copolymers suggest that this cobalt complex provides some degree of control over the copolymerization of VAc and MAF-TBE. Compared to the previously investigated cobalt complex OMRP mediators having a fully oxygen-based first coordination sphere, this study emphasizes a few peculiarities of Co(SAL)2: a lower ability to trap radical chains as compared to Co(acac)2 and the absence of catalytic chain transfer reactions, which dominates polymerizations carried in the presence of 9-oxyphenalenone cobalt derivative.
Fichier principal
Vignette du fichier
polymers-09-00702.pdf (2.71 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-01694075 , version 1 (27-05-2021)

Licence

Paternité

Identifiants

Citer

Sanjib Banerjee, Ekaterina Bellan, Florence Gayet, Antoine Debuigne, Christophe Detrembleur, et al.. Bis(formylphenolato)cobalt(II)-Mediated Alternating Radical Copolymerization of tert-Butyl 2-Trifluoromethylacrylate with Vinyl Acetate. Polymers, 2017, 9 (12), pp.702. ⟨10.3390/polym9120702⟩. ⟨hal-01694075⟩
109 Consultations
22 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More