Cementite-free martensitic steels: A new route to develop high strength/high toughness grades by modifying the conventional precipitation sequence during tempering - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Acta Materialia Année : 2012

Cementite-free martensitic steels: A new route to develop high strength/high toughness grades by modifying the conventional precipitation sequence during tempering

Denis Delagnes
M. H. Mathon
Raphaële Danoix
Frédéric Danoix
Pascal Lamesle
  • Fonction : Auteur
  • PersonId : 762052
  • IdRef : 14421735X
A. Grellier
  • Fonction : Auteur

Résumé

Aluminium was added to a 0.2% C-2.5% Cr-1.4% Mo-11% Ni steel to modify the precipitation sequence during tempering treatment. The main goal was to obtain fine co-precipitation of an intermetallic phase and M2C carbides (where M is a combination of Cr, Mo and small amounts of Fe). Small angle neutron scattering, synchrotron X-ray diffraction, transmission electron microscopy and atom probe tomography were performed to characterize the nanometric precipitation. The tempering response of samples austenitized at 900 degrees C revealed a strong interaction between the two types of precipitation, leading to a significant modification of both the precipitation sequence of carbides and the arrangement of carbide nucleation sites compared with these sites in a single precipitation steel. Indeed, a microstructural investigation clearly showed that iron carbide precipitation was either delayed or did not occur during the tempering process, depending of the alloying elements added. Moreover, double precipitation directly influenced the mechanical resistance, as well as the toughness, leading to an ultrahigh-strength, high toughness steel.
Fichier principal
Vignette du fichier
cementite-free-martensitic-steels.pdf (1.32 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01687325 , version 1 (15-03-2019)

Identifiants

Citer

Denis Delagnes, Florence Pettinari-Sturmel, M. H. Mathon, Raphaële Danoix, Frédéric Danoix, et al.. Cementite-free martensitic steels: A new route to develop high strength/high toughness grades by modifying the conventional precipitation sequence during tempering. Acta Materialia, 2012, 60 (16), pp.5877-5888. ⟨10.1016/j.actamat.2012.07.030⟩. ⟨hal-01687325⟩
153 Consultations
358 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More