SrCo0.85Fe0.15O2.62 -Oxygen deficient "314-type" perovskite; a highly efficient cathode for solid oxide fuel cells

Résumé

Structure, electrical conductivity and electrochemical performance for a new oxygen deficient perovskite material with composition SrCo0.85Fe0.15O2.62 is explored here. It crystallizes in a " 314-type " oxygen-vacancy ordered structure (Space Group: I4/mmm) with 2ap × 2ap × 4ap unit cell, and contains alternate oxygen replete [Co2/Fe2-O] and oxygen deficient [Co1/Fe1-O] planes along c-direction. Room temperature Mössbauer spectroscopy and room temperature neutron powder diffraction confirm the presence of mixed valence states (3+ and 4+) for both Fe and Co. Polaronic behavior in the electrical conductivity is observed below 400 °C, and attributed to the presence of Co 4+ and Fe 3+ cations in the structure. The electrical conductivity at 600 °C is high enough (∼200 S cm −1) to act as a cathode material. At the same time, the polarization resistance measurements show an excellent value of 0.1 Ω cm 2 at 600 °C. These results suggest that at 600 °C, this material is a mixed oxide-ion and electronic conductor exhibiting excellent activity for the oxygen reduction reaction, making it a promising cathode material for an intermediate temperature solid oxide fuel cell.

Domaines

Matériaux
Fichier principal
Vignette du fichier
17078.pdf (1.01 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01545868 , version 1 (23-06-2017)

Identifiants

Citer

Sourav Marik, Clément Nicollet, Madhu Channabasappa, Sébastien Fourcade, Alain Wattiaux, et al.. SrCo0.85Fe0.15O2.62 -Oxygen deficient "314-type" perovskite; a highly efficient cathode for solid oxide fuel cells. Fuel Cells, 2017, 17 (3), pp.353-358. ⟨10.1002/fuce.201600203⟩. ⟨hal-01545868⟩
157 Consultations
77 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More