Fretting fatigue crack propagation rate under variable loading conditions

Résumé

Fretting fatigue experiments aim to represent industrial problems and most of them endure variable loading. Being able to assess lifetime of assemblies, especially for low propagation rate conditions, is essential as experimental validation is often too expensive. Both experimental and numerical approaches are proposed to follow the crack propagation rate of steel on steel cylinder/plane fretting fatigue contact submitted to variable loading conditions. An original experimental monitoring has been implemented on the fretting-fatigue test device to observe crack propagation using a potential drop technique. A calibration curve relating crack length and electrical potential was established for the studied contact. It allows direct knowledge of the crack length and crack propagation rate. It was applied to mixed load test showing crack arrest for the last loading condition. To explain this behavior, a 2-dimensional FE modeling was implemented to simulate the complexes multi-axial contact stressing. The crack propagation rate was formalized using an effective stress intensity factor amplitude ΔKeff coupled with Paris law of the material. The crack arrest condition for a given loading was related to ΔKeff along the expected crack path crossing the material crack arrest threshold ΔK0. The failure was related to ΔKeff reaching the critical stress intensity factor KIC. A good correlation with experiments was observed allowing to predict the crack arrest condition although the model tends to overestimate the final crack length extension.

Dates et versions

hal-01526075 , version 1 (22-05-2017)

Identifiants

Citer

Camille Gandiolle, Siegfried Fouvry. Fretting fatigue crack propagation rate under variable loading conditions. Frattura ed Integrità Strutturale / Fracture and Structural Integrity, 2016, 35, pp.232-241. ⟨10.3221/IGF-ESIS.35.27⟩. ⟨hal-01526075⟩
79 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More