A novel PAN/silazane hybrid polymer for processing of carbon-based fibres with extraordinary oxidation resistance - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Journal of Materials Chemistry A Année : 2017

A novel PAN/silazane hybrid polymer for processing of carbon-based fibres with extraordinary oxidation resistance

L. F. B. Ribeiro
  • Fonction : Auteur
Olivier Flores
P. Furtat
  • Fonction : Auteur
R. Kempe
  • Fonction : Auteur
R. A. F. Machado
  • Fonction : Auteur
G. Motz
  • Fonction : Auteur

Résumé

A novel hybrid polymer made up of acrylonitrile (AN) and a commercial available oligosilazane (ML33) was developed as a precursor for the processing of carbon-based fibres with extraordinary intrinsic oxidation stability up to 800 degrees C. While polyacrylonitrile is used as the typical precursor for carbon fibres, a polysilazane derived SiCN ceramic phase should lead to improved oxidation resistance. Thermogravimetric analysis demonstrated that depending on the AN/ML33 ratio the weight loss during pyrolysis is drastically reduced up to 63% due to crosslinking reactions between both components, confirmed by NMR spectroscopy investigations. Unexpectedly, with increasing AN content in the starting composition the thermal treatment up to 1500 degrees C leads to a change from amorphous C/SiCN to C/Si3N4 nanocomposites confirmed by NMR, XRD and TEM measurements. The homogeneously distributed ceramic phase within the carbon matrix is responsible for the extraordinary intrinsic oxidation stability of this new type of carbon-based fibre.

Domaines

Matériaux
Fichier non déposé

Dates et versions

hal-01518198 , version 1 (04-05-2017)

Identifiants

Citer

L. F. B. Ribeiro, Olivier Flores, P. Furtat, C. Gervais, R. Kempe, et al.. A novel PAN/silazane hybrid polymer for processing of carbon-based fibres with extraordinary oxidation resistance. Journal of Materials Chemistry A, 2017, 5 (2), pp.720-729. ⟨10.1039/c6ta09293d⟩. ⟨hal-01518198⟩