Austenite arrest in polycrystalline Ni-Mn-Co-In films

Résumé

Electrical resistivity and magnetization measurements realized on polycrystalline Ni45.2Co4.7Mn36.2In13.9 film showed that the austenite phase was blocked upon a magnetic field during the martensitic transformation. Besides, the shift of the temperature transition upon a magnetic field towards the lower temperature is responsible for a large magnetoresistance that can be irreproducible in the heating branch of the transformation and that was measured in this work. We studied how the magnetoresistance was changing inside the hysteresis loop depending on whether the temperature lies on the forward or reverse transformation path. The analysis is interpreted in terms of the non equilibrium state consequent to the field cooled process and how martensite is converted into austenite inside the hysteresis loop when the magnetic field is applied.

Domaines

Matériaux
Fichier non déposé

Dates et versions

hal-01396398 , version 1 (14-11-2016)

Identifiants

Citer

Guillaume Crouigneau, Laureline Porcar, P. Courtois, P. Lachkar, Daniel Bourgault. Austenite arrest in polycrystalline Ni-Mn-Co-In films. Journal of Alloys and Compounds, 2017, 693, pp.700 - 704. ⟨10.1016/j.jallcom.2016.09.196⟩. ⟨hal-01396398⟩

Collections

UGA CNRS NEEL
66 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More