Influence of a transverse magnetic field on solidification structure during directional solidification

Résumé

Three alloys were directionally solidified at low growth speeds under a transverse magnetic field. The results show that the application of the transverse magnetic field significantly modified the solidification structure. Indeed, we found that along with the refinement of cells/dendrites, the magnetic field caused the deformation of liquid-solid interfaces, extensive segregations (i.e., freckles and channels) in the mushy zone. Moreover, we observed that dendrite fragments and equiaxed grains were moved approximately along the direction perpendicular to the magnetic field. Modification of the solidification structure under a weak magnetic field is attributed to a TEMC-driven heat transfer and interdendritic solute transport and a TEMF-driven motion of dendrite fragments.
Fichier principal
Vignette du fichier
6.53393.pdf (308.67 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01331369 , version 1 (13-06-2016)

Identifiants

  • HAL Id : hal-01331369 , version 1

Citer

Xi Li, Y Fautrelle, J Wang, A Gagnoud, Z. M. Ren, et al.. Influence of a transverse magnetic field on solidification structure during directional solidification. 8th International Conference on Electromagnetic Processing of Materials, Oct 2015, Cannes, France. ⟨hal-01331369⟩
256 Consultations
50 Téléchargements

Partager

Gmail Facebook X LinkedIn More