Efficient radiative recombination and potential profile fluctuations in low-dislocation InGaN∕GaN multiple quantum wells on bulk GaN substrates. - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Journal of Applied Physics Année : 2005

Efficient radiative recombination and potential profile fluctuations in low-dislocation InGaN∕GaN multiple quantum wells on bulk GaN substrates.

Résumé

We investigated the relation between structural properties and carrier recombination processes in InGaN∕GaNmultiple quantum well(MQW) structures with quantum well widths of 3 and 9nm, grown by metal-organic chemical-vapor deposition on bulk GaN crystals. Quantum barriers of the samples are heavily n-type doped in order to effectively screen the large polarization-induced electric fields which commonly occur in hexagonal InGaN∕GaN quantum structures. High thermal stability in these structures, reflected by strong photoluminescence(PL) even above 400K, is attributed to a combination of low-dislocation densities and potential profile fluctuations in the InGaN∕GaNquantum wells. The role of potential profile fluctuations is further investigated by time-resolved photoluminescence and cathodoluminescence(CL) mapping. Comparison of both samples shows that the sample with 3‐nm-wide QWs exhibits (i) a larger width of the PL peak in the temperature range of 8–420K, (ii) a higher amplitude of potential profile fluctuations as measured by CL mapping, and (iii) higher radiative and nonradiative PL recombination times. At the same time a much weaker drop of PL intensity with temperature is recorded on the sample with 9‐nm-wide QWs. Our results show that, contrary to intuitive expectation, a decrease of the potential profile fluctuation amplitude can be helpful in enhancing the radiative recombination efficiency, particularly at high temperatures.
Fichier non déposé

Dates et versions

hal-01304034 , version 1 (19-04-2016)

Identifiants

Citer

G. Franssen, S. Grzanka, Robert Czernecki, Tadeusz Suski, L Marona, et al.. Efficient radiative recombination and potential profile fluctuations in low-dislocation InGaN∕GaN multiple quantum wells on bulk GaN substrates.. Journal of Applied Physics, 2005, 97 (10), pp.103507. ⟨10.1063/1.1897066⟩. ⟨hal-01304034⟩
32 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More