Characterization of multi-walled carbon nanotube dispersion in resorcinol-formaldehyde aerogels

Ali Akbar Yousefi
  • Fonction : Auteur
Mohammad Jalal Zohouriaan Mehr
  • Fonction : Auteur
Alain Celzard
Vanessa Fierro
Nathalie Job
  • Fonction : Auteur
  • PersonId : 843267

Résumé

Multi-walled carbon nanotube (MWCNT)/resorcinol-formaldehyde (RF) composite gels were prepared by sol-gel polymerization of RF monomers in a suspension of carbon nanotubes in water, followed by CO2 supercritical drying. X-ray microtomography showed that the suspensions of MWCNTs were stable and that the distribution of nanotubes throughout the RF matrix was uniform. The level of MWCNT dispersion in the composites was evaluated by microscopic methods (optical microscopy, SEM and TEM). Micrographs showed that, at low MWCNT concentration (<0.26 v%), the nanotube bundles were completely exfoliated, leading to a homogeneous material at the nanometer scale. On the contrary, at higher concentrations, aggregates of MWCNTs with diameters up to 50 mu m were observed. N-2 sorption analysis showed that the carbon nanotube aggregation may result in a decrease of BET surface area of the composites. Thermal conductivity of the nanocomposites was measured by TPS hot disk method and the data were consistent with effective medium theory (EMT). At high MWCNT loadings, it was possible to estimate the volume fraction of separated and aggregated carbon nanotubes based on the deviation of the experimental conductivity data from EMT predictions.
Fichier non déposé

Dates et versions

hal-01295574 , version 1 (31-03-2016)

Identifiants

Citer

Majid Haghgoo, Ali Akbar Yousefi, Mohammad Jalal Zohouriaan Mehr, Alain Celzard, Vanessa Fierro, et al.. Characterization of multi-walled carbon nanotube dispersion in resorcinol-formaldehyde aerogels. Microporous and Mesoporous Materials, 2014, 184, pp.97-104. ⟨10.1016/j.micromeso.2013.10.002⟩. ⟨hal-01295574⟩
91 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More