Oxidative solution polymerization of aniline hydrochloride onto electrospun nanofibers mats of polylactic acid: Preparation method and characterization - Archive ouverte HAL Access content directly
Journal Articles Journal of Applied Polymer Science Year : 2014

Oxidative solution polymerization of aniline hydrochloride onto electrospun nanofibers mats of polylactic acid: Preparation method and characterization

Abstract

In this work, we present the preparation of polylactic acid (PLLA)/polyaniline (PANI) conductive composite nanofibers mats. They are prepared by bulk oxidative solution polymerization of PANI onto electrospun non-woven fibers mats of PLLA. The PANI ratio in the composite is about 70%w/w. Scanning electron microscopy (SEM) shows that PLLA nanofibers are randomly oriented, beads free with diameters of 186 ± 85 nm, The PLLA/PANI composite nanofibers diameter values are 518 ± 128 nm with a good adherence between PANI and PLLA nanofibers. DSC and XRD measurements reveal an amorphous structure of the electrospun PLLA fibers due to the rapid evaporization of the solvent. FTIR and UV-vis spectra reflect good mutual interactions between PANI and PLLA chains. The DC-conductivities (σ=0.07-0.13-S.cm-1) far better than other published ones for similar composites prepared by bulk oxidative solution polymerization of PANI onto other electrospun nanofiber mats or with electrospun nanofibers from a solution mixture of PLLA and PANI.
Fichier principal
Vignette du fichier
PIMM-JAP-ALJALLAD-2014.pdf (721.78 Ko) Télécharger le fichier
Origin Files produced by the author(s)
Loading...

Dates and versions

hal-01108954 , version 1 (02-02-2015)

Identifiers

  • HAL Id : hal-01108954 , version 1
  • DOI : 10.1002/app.41618
  • ENSAM : http://hdl.handle.net/10985/9267

Cite

Mazen Al-Jallad, Yomen Atassi, Eskandar Mounif, Matthieu Aressy, Abbas Tcharkhtchi. Oxidative solution polymerization of aniline hydrochloride onto electrospun nanofibers mats of polylactic acid: Preparation method and characterization. Journal of Applied Polymer Science, 2014, 132, pp.41618 (1-7). ⟨10.1002/app.41618⟩. ⟨hal-01108954⟩
87 View
284 Download

Altmetric

Share

Gmail Mastodon Facebook X LinkedIn More