Superledge model for interphase precipitation during austenite-to-ferrite transformation - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Metallurgical and Materials Transactions A Année : 2014

Superledge model for interphase precipitation during austenite-to-ferrite transformation

Résumé

A model for interphase precipitation has been developed based on the ledge mechanism of austenite-to-ferrite transformation. Carbide precipitation is considered on the migrating ferrite/austenite interface as an interaction of transformation and precipitation kinetics. The derived equations describe sheet spacing and particle spacing of interphase-precipitated carbides as well as the overall interface velocity which are related to the nucleation rates of carbides and ferrite ledges, respectively. The microstructure characteristics of interphase precipitation are predicted as a function of transformation temperature and steel composition and replicate trends observed experimentally.

Domaines

Matériaux
Fichier non déposé

Dates et versions

hal-01074752 , version 1 (15-10-2014)

Identifiants

Citer

Meng-Yang Chen, Mohamed Gouné, Matthias Militzer, Yves Bréchet, Jer-Ren Yang. Superledge model for interphase precipitation during austenite-to-ferrite transformation. Metallurgical and Materials Transactions A, 2014, 45 (12), pp.5351-5361. ⟨10.1007/s11661-014-2486-8⟩. ⟨hal-01074752⟩
115 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More